我国天然气探明未开发储量在全国已探明气田储量中占比超1/3，加快未开发储量的动用可促进天然气进一步上产稳产。基于我国天然气探明未开发储量的分布、特点及未动用的原因分析，建立了探明未开发储量分类评价方法、标准及流程，并进行了分类评价。我国天然气探明未开发储量以低渗透—特低渗透和碳酸盐岩非均质气藏储量为主，集中分布在四川、鄂尔多斯、塔里木盆地。未开发储量中，近期可动用储量占27.4%，难动用储量占58.4%，待核销储量占14.2%。我国难动用储量规模较大，在目前体制机制、技术经济及政策条件下无法动用，为此，从油气企业体制机制改革、管理与技术创新、国家政策等方面提出了加快我国难动用储量开发的具体举措与政策建议。     

Ni,Cr, and Fe surfaces corroded by molten ZnCl2

Understanding the corrosion of molten ZnCl₂ on metal surfaces is significant for the corrosion protection of metals, sustainable use of molten salts, preparation of ZnO coatings, and so on. In this paper, surfaces of pure Ni, Cr, and Fe corroded by molten ZnCl₂ were investigated. The results show that Ni suffered very slight corrosion, while Cr experienced more serious corrosion than Ni, but lighter corrosion than Fe. The morphology of the corrosion of Cr and Fe, respectively, presented pitting and intergranular corrosion characteristics. Furthermore, nanostructured ZnO coatings were obtained on the surfaces of Ni and Fe, but not on the surface of Cr. The ZnO coating on the Ni surface was doped with a small amount of Zn₅(OH)₈Cl₂, and the ZnO coating on the Fe surface was doped with ZnFe₂O₄ and Zn₂OCl₂. The coatings on the Ni and Fe surfaces had an average thickness of 1.5 and 50 μm, respectively.     

Dissimilar Metal Joining of 304 Stainless Steel to SMA490BW Steel Using the Filler Metal Powders with a High-Entropy Design

Metals and Materials International - High-entropy alloys having excellent properties are particularly suitable for the application as the filler metals in welding. In the present study,...     

Up-pulling force analysis for ESC hollow cylindrical casting

Electroslag casting(ESC)is an important method to produce high quality castings.In this study,the ESC up-pulling inner mold method(EUPIM)was used to produce hollow cylindrical castings with the multiple consumable electrodes.The radial deformation,the axial and radial internal stress of the inner mold,and the axial internal stress of the slag shell were analyzed using the finite element method(FEM)with the aid of ANSYS software.The ProCAST software was used to calculate the specific heat,heat conductivity and density curve of Cu.Simulation results show that the radial deformation,the axial and radial internal stress of the inner mold,and the axial internal stress of the slag shell near the slag-metal interface of hollow cylndrical casting gradually increase from 0 s to 360 s after the ESC starting(slagging)process but before applying the up-pulling force.The suitable initial up-pulling moment of the inner mold is at around 180-198 s after the starting process.     

基于SnO2中空纳米球的低温氢气传感器的研究

采用水热法一步合成SnO2纳米材料,采用XRD、SEM、TEM和氮吸附-脱附对材料的结构和形貌进行表征。表征结果表明所制备SnO2纳米材料是由直径150~200 nm的中空纳米球组成,且具有较大比表面积(82.6 m2/g)。采用丝网印刷技术将SnO2气敏浆料涂覆到叉指电极上,制成厚膜型气体传感器器件,研究其对氢气的气敏性能。结果表明SnO2中空纳米球在较低温度(200℃)下对5~200μl/L氢气具有较高的响应值及较快的响应速度,这归因于所制备的SnO2材料的中空结构和较大比表面积,利于氢气气体的吸附与扩散。     

哈氏合金X电子束表面处理微观组织研究

哈氏合金因其优良性能被广泛应用于航空工业,利用强流脉冲电子束(HCPEB)轰击哈氏合金X表面对其进行改性,并对其显微组织进行分析和讨论。利用扫描电子显微镜(SEM)观察腐蚀后试样,利用电子背散射衍射(EBSD)观察未腐蚀试样。结果表明：从扫描电镜照片可以看到,未轰击试样晶界被腐蚀,轰击后试样表面存在约为2μm的重熔层,腐蚀程度减轻,晶界处出现颗粒状碳化物；从EBSD结果可知,轰击5次试样晶粒尺寸最小,轰击5次和10次试样晶粒取向性更好,多为[101]和[110]。实验表明强流脉冲电子束轰击能够使哈氏合金X表面出现重熔层,并改变其晶粒大小和晶体取向。     

AZ31镁合金薄板经不同累积应变的连续弯曲变形后的显微组织与成形性能

对AZ31镁合金板材进行不同累积应变的连续弯曲变形及退火处理,随后对显微组织与力学性能的变化进行了研究。结果表明:经不同累积应变的连续弯曲变形后,镁合金板材的显微组织中没有发现孪晶,退火后,板材表层的晶粒异常长大,粗晶层的厚度随着累积应变的增加而增加,并且镁合金板材的织构朝RD方向偏转,偏转角度随累积应变的增加而增大;与原始板材相比,连续弯曲变形及退火处理使镁合金板材呈现出较好的室温成形性能(杯突值由2.3 mm提高到4.9 mm,提高了~113%),这主要归因于基面织构的改善使镁合金板材的r值减小与n值增大。     

Effects of stray AC on corrosion of 3-layer polyethylene coated X70 pipeline steel and cathodic delamination of coating with defects in 3.5 wt-% NaCl solution

In this work, the effects of stray alternating current (AC) on the corrosion of coated X70 pipeline steel and the delamination of 3-layer polyethylene (3PE) coatings with defects were investigated using COMSOL Multiphysics simulation, electrochemical impedance spectroscopy and three-dimensional (3D) digital microscope techniques. The results showed that under the same level of AC interference, pits with deeper maximum pit depth were observed at the smaller defect areas than those at larger defect areas. It was consistent with the simulation results that a greater corrosion current density was accompanied on samples with smaller defects. According to 3D digital images, the larger delamination of 3PE coatings was found on samples with smaller defects. With the increase of current density, the impedance of samples with small defects decreased, while that of samples with large defects increased. Additionally, with the same defect size, the maximum pit depth became deeper and the corrosion was more severe.     

In-situ formation of BN layers by nitriding boron powders in BN/Si3N4-based composite ceramics

Boron nitride/silicon nitride (BN/Si₃N₄) composite ceramics were fabricated via the in-situ nitridation of boron (B) and silicon (Si) powders in forming gas (95%N₂/5%H₂) at 1390?°C. The effect of the B content on the phase composition, microstructure, density/porosity, machinability as well as mechanical properties of nitridized BN/Si₃N₄ composite ceramics was investigated. The addition of B slightly increased the nitridation degree of the Si and B powders mixture, and improved the ratio of the β-Si₃N₄ phase significantly at low B contents. B powders may have acted as a nucleating agent to promote the formation of β-Si₃N₄ crystals. A core-shell Si₃N₄/BN structure was revealed by the TEM technique, and the number of BN layers increased with the increase of the B content. The in-situ BN formed by the nitridation of B played a similar role with the BN directly added in enhancing the machinability of the BN/Si₃N₄ composite ceramics. The method of the in-situ nitridation of B is also effective to prepare SiC fiber-reforced BN/Si₃N₄ ceramic matrix composites.     

MOCVD-derived GdYBCO tapes with smooth surface and low Rs based on a new self-heating technology

The metal organic chemical vapor deposition (MOCVD) method was used to prepare GdYBCO films on LaMnO₃/ homo epitaxial-MgO/ ion-beam-assisted-deposition-MgO/ solution-deposition-planarization-Y₂O₃ buffered Hastelloy tapes. By adopting a simple self-heating technique, the substrates were heated by the joule effect after applying a heating current (I_h) through Hastelloy metal tapes. The effects of substrate temperature and (Gd, Y)/Ba ratio (r_c) in the precursor on the biaxial texture, surface morphology and superconducting performance of GdYBCO films were systematically investigated by varying the values of I_h and r_c. Needle-like outgrowths formed on the substrate surface were characterized using a scanning electron microscope, energy dispersive spectrometer and X-ray diffraction system. The results show that a high I_h or r_c leads to the formation of needle-like outgrowths. Therefore, I_h and r_c are crucial process parameters that control the growth of needle-like outgrowths on the surface of GdYBCO films. Three hundred nanometer thick GdYBCO films were prepared at different I_h and r_c by the MOCVD process. At an I_h of 27.0?A and an r_c of 0.6, the surface of the GdYBCO film was very smooth and dense, which can provide a good template for multiple depositions of GdYBCO films. The critical current density of the deposited 300?nm-thick GdYBCO film was 4.4 MA/cm² (77?K, 0?T), which is attributed to good biaxial texture and appropriate film composition. Furthermore, the microwave surface resistance (77?K, 10?GHz) of the GdYBCO film was merely 0.581?mΩ.